In this study, several nickel catalysts for the steam-hydrocarbon reforming process were prepared from various nickel salt, magnesium oxide, alumina and kaolinite. The activity and strength of the catalysts were investigated. 1. The proper composition of the calcined catalysts are: NiO (5-15%)-MgO(10-20%)-$Al_2O_3$(10-40%)-Kaolinite(50-80%). 2. The admixed or cosedimented ingredients of the catalysts was pelletized and calcinated at 1000 or $1150^{circ}C$. Calcination at $1150^{circ}C$ for an hour was optimum. 3. The water to oil ratio (W/O) for reforming of hexane should be above 7 mole/mole. As the W/O increases, more carbon dioxide and hydrogen, but less carbon monoxide was produced. Also carbon deposition become lessen at higher W/O. 4. Maximum conversion had attained at about $850^{circ}C$. As the reaction temperature increases, more carbon monoxide and hydrogen, but less carbon dioxide and lower hydrocarbon was produced. 5. The percent conversion at $850^{circ}C$ was about 80%, using a catalyst which the nickel oxide content are 5%.