This investigation was performed to evaluate the effect of four different preteatment techniques on the bond strength of porcelain to non-precious metal alloy. Samples of total of 40 were divided into 4 groups according to the 4 variables which included the 50$mu$alumina oxide air abrasion, method, the as retention bead method, the L-retention bead method, the Etching method. The completed metal-porcelain samples were compressed in Instron loading machine until gross fracture occured to examine the effect of the complex variables on the bond strength of porcelain to non precious metal alloy. The result obtained were as follows : 1. The difference of bond strength according to four different pretreatment techniques was statistically significant(p<0.01). 2. The difference of bond strength between the ss-retention bead method and the L-retention bead method was not significant statistically(p>0.05) 3. The difference of bond strength between the retention bead method and the etching method was statistically significant(p<0.01). 4. The difference of bond strength between the retention bead method and the 50$mu$alumina oxide air abrasion method was statistically significant(p<0.01). 5. The difference of bond strength between the etching method and the 50$mu$alumina oxide air abrasion method was statistically significant(p<0.01).