Experiments on electorchemical etching of aluminum foils with high cubic textures were carried out in this study. Etching behaviours and pit shapes with respect to various conditions of eletrochemical etching were in-vestigated. When HCl and NaCl solutions were used as electrolytes, the highest capacitanes were observed in solutions of 1MHCl and 5M NaCl. It was foundd that capacitance was improved by addition of H2SO4 to HCl so-lution which is considered to be due to the suppression of oxide film formation on the aluminum surface. The homogeneous distribution of each pits obtained in the HCl solution, while the degree of weight loss was lowest in the Nacl solution. The best etching properties in 1M HCl solution were obtained at the etching condi-tions of 0.15 A/$ extrm{cm}^2$, 150sec and$ 90^{circ}C$.