The effects of electrolysis conditions on the composition and preferred orientation of Ni-Fe alloy were studied using the sulfate-chloride baths paddle agitated. Cathode current efficiency is higher in the deposits from bath 2 than that of deposits from bath 1. The Fe content of alloy deposits from bath 2 is nearly constant(19∼21wt.%) in the wide range of current density, while it decreases noticeably with current density in the deposits from bath 1. The variation of Fe content at the edge of specimen is lower in deposits from bath 2 than those from bath 1. The alloy deposits show (111) & (200) preferred orientation for the deposits from bath 1 and bath 2 respectively.