Emulsion graft copolymerizations of vinyl monomers, butyl acrylate(BA), methyl methacrylate(MMA), 2-ethylhexyl acrylate (EHA), glycidyl methacrylate (GMA), 2-hydroxyethyl methacrylate(HEMA), methacrylonitrile(MAN), dimethylaminoethyl methacrylate(DAMA) or 2-vinyl pyridine(VP), onto carboxyl-terminated SBR latex were carried out under different experimental conditions. In case of synthesizing SBR-g-poly(butyl acrylate), the degree of grafting was increased with increasing the amount of emulsifier, polymerization temperature and the amount of initiator. Pull-out strength of resorcinol-formaldehyde-latex(RFL) adhesives formulated with modified latexes was very higher than that of RFL adhesive formulated with ungrafted latex. When the modified latexes with GMA, HEMA, MAN, DAMA or VP were used, the break occurred at cords. Peel strength of RFL adhesives formulated with SBR-g-poly(GMA), SBR-g-poly(HEMA) or SBR-g-poly(VP) was higher by about 1.3 times than that of RFL adhesives formulated with unmodified SBR against nylon cord and was higher by about 2.0 times against polyester cord.