In this paper, fatigue crack propagation behaviors were investigated experimentally for the materials, carbon steel forgings (SF45A, SF50A, SF60A) which are used in the marine propeller shaft. The results obtained are as follows: The number of cycles required to grow crack length 1.30mm from microcrack initiation was about 60% of the total fatigue life. Fatigue crack propagation rate was expressed by the equation d(2a)/dN_B 2a/$N_f$ and the result was agreed well with the experimented data. And the equation d(2a)/dN=$C{sigma}_a^m(2a)^n$ was evaluated also. Obtained material property m and n are 3~5 and 1-1.5 respectably, and the result was reasonably agreed to the data obtained from experiments.