A kinetic study on the electrodeposition of Ni-Zn-P ternary alloys onto a steel in chloride solutions was carried out using a rotating disc electrode. The coatings were characterized using SEM/EPMA and A. A. analysis. The results showed that the plating rates of three components were increased with applied potential, disc rotating speed and temperature. The activation energies of Ni, Zn and P of the coatings were 6.1, 5.1 and 8.0 kcal/mole respectively. Therefore, the deposition rates were controlled partly by surface electrochemical reaction and partly by mass transport. As the potential, temperature of bath and rotating speed of cathode disc were raised, the vol. % ratios of Ni and P of coating layer were increased but that of Zn decreased. The effect of coating parameters on the surface morphology was also examined.