Coupling optical modulator which on the $LiTaO_3$ substrate is fabricated by using proton exchange method and self-aligned method. Proton exchange of proton diffusion method was applied to pattern a waveguide on $LiTaO_3$ substrate. The annealing at >$400^{circ}C$ was carded out to control waveguide width and depth. The depths of the two annealed optical waveguides, which were measured by using .alpha.-step, were 1.435 K.angs. and 1.380 K.angs. Using .alpha.-step facility, we examined that the width of waveguides is increased from 5.mu.m to 6.45 .mu.m and 6.3.mu.m due to the annealing effects. The process of proton exchange was done at 150.deg. C for 120 min, >$200^{circ}C$</TEX> for 60 min and annealing process was done at >$400^{circ}C$ for 90 min, >$400^{circ}C$</TEX> for 60 min. The high speed coupling optical modulator has very good figures of merits; the measured high frequency power were achieved.