The green emitting phosphors of the Field Emission Display(FED), Al codoped ZnGa$_{2}$O$_{4}$:Mn, were synthesized and sintered at high temperature. From X-ray diffraction measurements, it was confirmed that poly crystalline ZnGa$_{2}$O$_{4}$ and ZnAI$_{2}$O$_{4}$ solid solution coexist in Al codoped ZnGa$_{2}$O$_{4}$:Mn. Photoluminescence spectra of Al codoped ZnGa$_{2}$O$_{4}$:Mn show that the main peak position is shifted from 504 nm to 513 nm with the increase of Al concentration. The brightness was improved with the amount of Al dopant. It showed the maximum value at the doping level of 0.03 mole and then, it degraded rapidly. These results are due to the superposition of emission from . ZnGa$_{2}$O$_{4}$:Mn and ZnAI$_{2}$O$_{4}$:Mn.