Good appearance of insulation coating is required for non-oriented silicon steel sheets, The property is influenced by both the chemical composition of coating solution and the species of resin. The composition of inorganic-organic coating was studied to obtain good surface quality for non-oriented silicon steel. The greenish degree of coating surface depended on <tex>$Cr^{3+}$</tex> content in the coating layer, which was satisfied when chromate content was more than 54.60 wt. %, in the coating solution. The homogeneous pattern and roughness of the coating surface depended on spreading property of the resin. Surface appearance of the coating could be improved by using resin with good spreading property at the chemical composition of chromate 59.00 wt.%.. resin 34.23wt.%, and etyhylene glycol 6.67 wt.% without colloidal sillica.