In this experiment well-know additives for Mn-Zn ferrites CaO and {{{{ { SiO}_{2 } }} were added at various content and their effects on microstructures and magnetic properties with sintering atmosphere were examined. By adding up to 0.04wt% {{{{ { SiO}_{2 } }} and and 0.06wt% CaO the sintered density was increased and then decreased gra-dually. Higher sintered density and initial permeability were observed by adding both CaO and {{{{ { SiO}_{2 } }} than by adding CaO or {{{{ { SiO}_{2 } }} alone. Without any additives initial permeability and tan$delta$/${mu}$ decreased at 1000kHz as oxidation degree(${gamma}$) increased.