The fatigue life tests were performed in strain control with triangular and hole-time wave-forms at $650^{circ}C$. The fatigue lifes were investigated according to waveform examining damage mechanisms, which could be used to predict the fatigue life and estimate the remaining life. The results obtained are as follows; The fatigue lifes were in order of the fast-fast>the fast-slow>the slow-fast in the triangular waveforms, and the fatigue lifes in slow-fast waveforms got shorter in the hold-time waveforms. The damage mechanisms of the fracture surfaces were transgranular fracture in the fast-fast, the fast-slow waveforms and intergranular fracture in the slow-fast waveform.