The sample made of $Mn_3O_4$ indicated an excellent frequency dependency for intial permeability and core loss. Moreover the homogeneity of cation configuration in he spinel structure was confirmed by X-ray diffraction analysis. The result of homogeneity of the spinel structural coincided with the analytical results of temperature dependence of magnetization. Furthermore, the influence of manganese oxide as starting material, on homogeneity of spinel structure was examined by using thermogravimetry-differential thermal analysis. It may be concluded that the reaction between $Mn_3O_4$ and Fe-Zn oxide mixture proceeds at fist in all combination of manganese oxide and oxie mixture, and then Mn-Zn-Fe spinel was formed.