The friction characteristics of phenolic resin and model friction materials were investigated with the content of hexamethylenetetamine (HEXA). At 10 wt.% of HEXA, the phenolic resin and model friction materials showed the most stable friction coeffcient in constant temperature test at various test conditions because of its good thermal stability and proper curing reaction. It was found from constant interval test in mild condition that the friction coeffcients of friction materials cured with 10 wt.% of HEXA was the highest and stable values in the whole range of braking operations. However, at the severe condition in constant interval test, the friction coefficient of friction materials cured with 10 wt.% to of HEXA was lowered and as the number of braking operation increased, the values became stable. In order to obtain the thormal stable friction materials, the content of HEXA from 5 to 10 wt.% could be recommended.