The stochiometric mixtures mixture of evaporating materials for the $ZnIn_{2}S_{4}$ single crystal thin film was prepared from horizontal furnace. To obtain the $ZnIn_{2}S_{4}$ single crystal thin film, $ZnIn_{2}S_{4}$ mixed crystal was deposited on throughly etched semi-insulting GaAs(100) in the Hot Wall Epitaxy(HWE) system. The sourceand substrate temperature were $610^{circ}C$ and $450^{circ}C$, respectively and the growth rate of the $ZnIn_{2}S_{4}$ single crystal thin film was about 0.5$mu extrm{m}$/hr. The crystalline structure of $ZnIn_{2}S_{4}$ single crystal thin film was investigated by photoluminescence and double crystal X-ray diffraction (DCXD) measurement. The carrier density and mobility of $ZnIn_{2}S_{4}$ single crystal thin film measured from Hal effect by van der Pauw method are $8.51{ imes}10^{17}{ extrm}{cm}^{-3}$, 291$ extrm{cm}^2$/V.s at $293^{circ}$K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $ZnIn_{2}S_{4}$ single crystal thin film, we have found that the values of spin orbit splitting $Delta$So and the crystal filed splitting DCr were 0.0148eV and 0.1678 eV at $10^{circ}$K, respectively. From the photoluminescence measurement of $ZnIn_{2}S_{4}$ single crystal thin film, we observed free excition($E_{X}$) typically observed only in high quality crystal and neutral donor bound exicton ($D^{circ}$, X) having very strong peak intensity. The full width at half maximum and binding energy of neutral donor bound excition were 9meV and 26meV, respectively. The activation energy of impurity measured by Haynes rule was 130meV.