This research concerns the effect of kaolin as material of cement admixture. which has the advantage of low price and high adaptability. Kaolin, a kind of soil, is well known as a raw material of pottery. which is widely scat-tered on the earth (especially in Korea). This research shows the method and process for activating kaolin to have the properties of a cement admixture through experiment. In the experiments, kaolin is baked in high temperature and then cooled suddenly to be activated. The temperature zone and time span, on which kaolin is activated are examined. The research looks over the effect of the activated kaolin based on several criteria regarding to chemical and physical characteristic of general admixtures. The results of this research are as follows; kaolin start activation at the temperature above 50$0^{circ}C$ and make ends of activation at the temperature below 95$0^{circ}C$ and there was little effect by the change of duration. It is concluded that compressive strength can be increased by putting activated kaolin in the concrete and the activated kaolin is good for water resistance and anti-chemical , and that it is effective for protecting the leakage of hazardous article like Cl- and for protecting damage by an organic salt like acid. The activated kaolin of proper temperature and time is effective in compressive strength, salt resistance and acid resistance. The adaptability of activated kaolin as a cement admixture was shown through this research.