Ultrafiltration membranes base on copoly(amide-imide) derivatives were prepared by the phase inversion method and the factors determining the permeation characteristics of membrane were investigated. The permeation behavior was observed by the relative ratio of permeate flux (J$\_$t/)/pure water flux (J$\_$o/). The characteristics through membrane were measured using aqueous solution of poly(ethyleneglycol) (MW 2.0$ imes$10$^$4/) over a temperature range of 10∼90$^{C}$. With increasing the operating temperature, the relative ratio of flux became high. All the membranes had good chemical stability. Copoly(amide-imide) membranes having various Permeation properties could be obtained. Further, it was proved that the membrane performances could be determined from the preparation conditions as well as various operating conditions.