The solidification and leaching characteristics of cyclone ash collected from an industrial incineration plant were investigated. Cement and calcium hydroxide were used as the solidifying materials. The leaching characteristics of the solidified cyclone ash were found to vary depending on both the quantitative and the qualitative aspects of the solidifying materials. Except for copper and lead, all the heavy metal ions in the leachate of the solidified material composed of 10~20 % cement or 10~20 % calcium hydroxide were found to be within their standard limit. Moreover, all the heavy metal ions were also observed to be within satisfactory limits in the leachate obtained from the solidified material composed of 30 % cement or 30 % calcium hydroxide. Therefore, to satisfy the standard compressive intensity and permissible limits of heavy metal ions leached from solidified material, it would appear that a 30 % proportion of either additive in the solidification product can meet the required standard for the leachate. The cost of solidifying cyclone ash per ton for ash-30 % cement and ash-30 % lime was calculated as 26,750 and 26,070 won, respectively. Accordingly, significant reduction in the waste toxicity and mobility as well as an improvement in the engineering properties of the solidified products were successfully achieved.