Nickel powders were obtained by various preparation methods, and their sintering characteristics were investigated. Nickel powders made by wet chemical process (WCP) had a higher surface area and more narrow size distribution than that of chemical vapor deposition (CVD) method. Nickel-oxide powders by the WCP method were prepared at $200^{circ}C$ for 3 hr. The oxidation behaviour of nickel-oxide powder is similar with that of the CVD method. Nickel powders made by the WCP method showed a higher shrinkage in the range of $600^{circ}C$∼$900^{circ}C$ than that of commercial powder made by the CVD method. The similar results were observed on the surface microstructure of sintered bodies by SEM measurements.