0.91 (PSN-PZT) －0.05BF －0.04PNW＋0.3wt%MnO$_2$＋0.6wt%CuO＋xwt%CeO$_2$ ceramics were fabricated with the variations of CeO$_2$addition at the sintering temperature of 95$0^{circ}C$ and their microstructure, dielectric and piezoelectric characteristics were investigated. As the amount of CeO$_2$ addition increased, the grain size, density and electromechanical coupling factor(k$_{p}$) were increased and the mechanical quality factor(Q$_{m}$ ) was decreased. At the 0.3 wt% CeO$_2$, the density, grain size, electromechanical coupling factor(k$_{p}$), and pizoelectric constants(d$_{33}$, g$_{33}$) showed the maximum value of 7.87 g/㎤, 3.22 $mu extrm{m}$, 0.5, 289 pC/N, and 22.2 ㎷ㆍm/N, respectively. However, mechanical quality factor(Q$_{m}$ ) showed the minimum value of 807 at the 0.5 wt% CeO$_2$.$</TEX>.EX>.EX>.