Molybdate chemical conversion coating layer formed on EGI has been studied in view of corrosion resistance, surface morphologies, and phases formed. It was found that coating layer consists of$ MoO_3$, $MoO_2$, Mo oxides having lower valences than 4 and ZnO. It is interesting to note that the coating layer formed at high Mo concentration (30 g/l) in the temperature range of $40-60^{circ}C$ exhibited relatively high corrosion resistance, although thickness of coating layer is nearly identical with those formed under the other conditions. It was believed that an increase of driving force due to high Mo concentration plays an important role in the formation of corrosion-resistant coating layer, probably due to tile formation of dense coating layer.