The glass-forming conditions are investigated in the $K_2$O-CaO-$SiO_2$ $-P_2$$O_{5}$ system with 10~65 mole% of$ P_2$$O_{5}$. Thermal properties and dissolution properties were investigated according to variation of the SiO and KO contents in selected compositions. The glass formation condition was determined when $K_2$O/$P_2$$O_{5}$ mole ratio 0~0.24, $SiO_2$/($SiO_2$+$P_2$$O_{5}$ ) mole ratio 0～0.29, and CaO/$P_2$$O_{5}$ mole ratio 0~1.00. In the result of the thermal properties, the glass transition temperature($T_{g}$) and softening temperature($T_{s}$ ) were gradually shifted to the lower temperature range with increase of $K_2$O contents. The maximum value of the chemical durability was shown in $K_2$$PO_2$$O_{5}$ mole ratio 0.17 when the $SiO_2$ contents were changed, and $K_2$O was fixed at 10 mole%. Hence the change of the $K_2$O/$P_2$$O_{5}$ mole ratio was found that a new main factor of the chemical durability.