This study was carried out to obtain the basic data for producing higher functional coating agents for pulp mold by evaluating various kinds of starch derivatives. At that time, four kinds of starch derivatives were manufactured for making coating agents respectively. Physical properties of coated paperboards were tested. Conclusions obtained from this results were as follows. The water and oil resistance of hydroxypropylated, cyanoethylated and carboxymethy­lated starch were high when degree of molar substitution(DS) of propylene oxide, acrylonitrile and sodium monochloroacetate were 0.18, 0.07 and 0.009, respectively. Also, the those of crosslinked starch were high when degree of crosslinking of epichlorohydrin was 0.02. Consequently, $8\%$ solution of carboxymethylated starch made with DS 0.009 of monochloroacetate was the best among coating agents from starch derivatives men­tioned above.