Proton conducting composite membranes were prepared by solution blending of poly(vinylidene fluoride-co-chlorotrifluoroethylene)-graft-poly(sulfopropyl methacrylate) (P(VDF-CTFE)-g-PSPMA) graft copolymer and heteropolyacid (HPA). The P(VDF-CTFE)-g-PSPMA graft copolymer was synthesized by atom transfer radical polymerization (ATRP) using direct initiation of the secondary chlorines of P(VDF-CTFE). FT-IR spectroscopy revealed that HPA nanoparticles were incorporated into the graft copolymer via hydrogen bonding interactions. The water uptake of membranes continuously decreased with increasing HP A concentration up to 45wt%, after which it slightly increased. It is presumably due to the decrease in number of water absorption sites due to hydrogen bonding interaction between the HP A particles and the polymer matrix. The proton conductivity of membranes increased with increasing HPA concentration up to 45wt%, resulting from both the intrinsic conductivity of HP A particles and the enhanced acidity of the sulfonic acid of the graft copolymer.