Electrochemical deposition characteristics of CdSe nanorods were investigated for hybrid solar cell applications. CdSe nanorods were fabricated by electrochemical method in $CdSO_4$ and $H_2SeO_3$ dissolved aqueous solution using an anodic aluminum oxide (AAO) template. Uniformity of CdSe nanorods was dependent on the diameter and the height of holes in AAO. The current density, current mode, bath composition and temperature were controlled to obtain a 1:1 atomic composition of CdSe. CdSe nanorods deposited by direct-current method showed better uniformity compared to those deposited by purse-current and/or purse-reverse current methods due to the bottom-up filling characteristics. $H_2SeO_3$ concentration showed more significant effects on pH of solution and stoichiometry of deposits compared to that of $CdSO_4$. A 1:1 stoichiometry of uniform CdSe nanorods was obtained from 0.25M $CdSO_4-5$ mM $H_2SeO_3$ electrolytes with a direct current of 10 $mA/cm^2$ at room temperature. X-ray diffraction and electron diffraction pattern investigations demonstrate that CdSe nanorods are a uniform cubic CdSe crystal.