In this study, piezoelectric and dielectric properties of Lead-free $0.97[(K_{0.5}Na_{0.5})(Nb_{0.97}Sb_{0.03})O_3]+0.03[(Bi_{0.5}K_{0.5})TiO_3]$ (abbreviated as 0.97NKNS-0.03BKT)ceramics synthesized by conventional solid-state reaction process were investigated as a function of $K_{5.4}Cu_{1.3}Ta_{10}O_{29}$ addition. The results indicated that the $K_{5.4}Cu_{1.3}Ta_{10}O_{29}$ addition significantly improved the sinterability, grain growth and piezoelctric properties of 0.97NKNS-0.03BKT ceramics. The optimum values as planar piezoelectric coupling coefficient ($k_p$= 0.355), piezoelectric constant ($d_{33}$= 207 pC/N) and mechanical quality factor ($Q_m$= 128) were obtained when 0.009KCT was added. The electromechanical coupling factor($k_p$) was slightly decreased according to the increasing temperature.