Hollow mesoporous carbon nitride material with sphere shape was synthesized using polystyrene sphere as template and cyanamide as nitrogen and carbon atom sources via thermal treatment process. The process of the silica removal is not necessary because silica as template is not in use for the synthesis of hollow mesoporous carbon nitride material and any solvents are also not in use. The size of polystyrene spheres was about 170 nm. Hollow diameter and wall thickness were 82 nm and 13 nm, respectively, in hollow mesoporous carbon nitride sphere. Surface area, mesopore size and pore volume of hollow mesoporous carbon nitride material was $188m^2g^{-1}$, 3.8 nm and $0.35cm^3g^{-1}$, respectively. The wall in hollow sphere has graphitic structure. Hollow mesoporous carbon nitride material has potential applications in the area of fuel cell, catalysis, photocatalysis, electroemmision device, etc.