There are two problems to be solved by our efforts in the enamel frit. One is how we can cover the enamel frit thin with complete milk white as possible, and the other is how it can be, made resistant for chemicals than before one. The frit which can solved the two problems just mentioned above is titanium enamel frit. This frit has been developed in America after War Ⅱ, and now the research for concerning antimony frit into titanium frit is under development entirely. In order to develope the enamel industry in Korea, it is urgent problem to convert antimony frit into titanium frit. By the way the titanium frit is emulsified titanium oxide crystal which made through reheating the supersaturated solution of titanium oxide in the basis of glass. Unfortunately, there are many obscure points in active fact or which influence on its composition and characteristics yet. However, this task was tried for the first in Korea. As first step, the test was carried on the reference books, and we can be possible convert antimony frit into titanium frit as a result of this experiment. As a conclusion, for the purpose of developing the enamel industry in Korea, we studied that the research for converting antimony enamel frit which has been used popularly into titanium enamel frit which is more economic and resistant for chemicals. As a result of experiments, the following points concerning with titanium frit have become clearly. 1. It is better when the composition of titanium enamel frit has as following table.Man Duck San Silica 24 An Yang Feldspar 20 Borax 28 Sodium Nitrate 4 Cryolite 7 Calcium Carbonate 3.6∼1 Titanium Oxide 10 Calcium phosphate 0 ∼3.2 Calcium Fluoride 0∼1.8 Antimony Oxide 0∼0.5 2. The amount of $TiO_2$, to be added is $10%;to;12{%,;CaF_2;is;under;1.8%,;P_2O_5;is;under;1.6%,;Sb_2O_3;is;under;0.5%$. 3. In the titanium frit, the limit of iron oxide amount to be included is under 0. 5%. 4. Comparing the titanium enamel frit with antimony enamel frit not only the titanium frit can be savely 20.6% in the price of raw materials, but one time of glazing and heating process is omitted in each case, and it is known the titanium frit is more resistant for chemicals than antimony frit.