This experiment was conducted, how making use of "Seracol 100", a kind of nonionic surface active reagent, during cocoon cooking and silk reeling process which is mainly used in Korea and developed by one of the authors since 1965. Main purpose of the experiment is to investigate the influence of the activity of the reelability aid reagent on various degree of hardness component and various salts which are contained in filature water being used by silk factories now. Specifically, it was tried to determine the effects of the reelability aid reagent added to each sample water of artificially differentiated the degree of hardness component upon sericin solubility. Some of the major findings are summarized as follows. 1. "Seracol 100", with below 5$^{circ}$dH water, increased sericin solubility in each sample water, but above $10^{circ}$dH the effect of it shows a significant relationship with the different degree of hardness component. Besides the component (MgCO$_3$)$_4$ㆍMg(OH)$_2$, generally, the higher the degree of hardness in the water, the less the amount of desolved sericin in the water showed. There is little or no difference between 1000 times diluted "Seracol 100" water and 2000 times diluted "Seracol 100" water in terms of sericin solubility. 2. The different kind of degree of hardness component shows a significant relationship with sericin solubility, In case use of "Seracol 100", Mg hardness component affected on the sericin solubility more than Ca hardness. But in the control, contrary to this, that is Ca hardness component did more than Mg hardness, 3. The different kind of salts in degree of hardness component show a significant relationship with sericin solubility. In the control water, nitrate is the greatest among salts affecting on sericin solubility, next chloride and sulfate are in order. In case of "Seracol 100" water, chloride is the least among salts, below $10^{circ}$dH, next sulfate and nitrate are in order, and above 15$^{circ}$dH, next nitrate and sulfate are in order. 4. In case of "Seracol 100" water, the more contained heavy metal salts (Fe, Al, Cu, Mn) in the water, the less sericin solubility showed. It is found that there is little or no difference among other salts in terms of sericin solubility. But alkaline metal salt remarkably increased sericin solubility. 5. In case of "Seracol 100" water, tinting of the water was affected by Ca salts more than by Mg salts. Among other salts, only Al and Fe affected on the tinting of the water, specifically, in view of the fact that "Seracol 100" water increase the tinting of Fe salt water, but decrease the tinting of raw silk. It is thought that "Seracol 100" deter Fe$^{+2}$ from absorbing to raw silk by deteriorating the activity of Fe$^{+2}$ . 6. "Seracol 100" have the effect on osmosis of the water, After treatment until 2hrs the osmosis of 1000 times diluted "Seracol 100" water is the greatest, next orders are 2000 times diluted "Seracol 100" and control. From 2 hrs to 6 hrs the osmosis of 2000 times diluted water is the greatest, next orders are 1000 times diluted water and control. After 6 hrs the osmosis of the water is the same order as above. 7. In view of tile fact that "Seracol 100" have the effect to control the degree of hardness during the treatment of cocoon layer in the water, it is thought that, in varying degree of hardness in the water, there is a significant relationship between "Seracol 100" and degree of hardness components in cocoon layer.