There are some repels in which they studied on the change of acid-consuming capacity of aluminium hydroxide resulted from the passing of time. However, the relationship between grain sizes(particle sizes) and the acid-consuming capacity of dried aluminium hydroxide gel was not been studied. And studies on the grain sizes of aluminium hydroxide gel qualified by pharmacopoeia of Korea has not been reported. For the purpose of studying these two problems, the author prepared two-kinds of aluminium hydroxide gel as follows : $Na_2OAl_2O_3+CO_2------{longrightarrow}Al(OH)_3{cdots}{cdots}{cdots}$sample 1 $Al_2(SO_4)_318H_2O+6NaHCO_3{longrightarrow}Al(OH)_3{cdots}{cdots}{cdots}$sample 2 Both of sample 1 and 2 are found to be amorphous by X-ray diffraction methods, and their acid-consuming capacities were determined by the method of pharmacopeia of Korea. The grain size was measured by X-ray diffraction method, the particle sizes observed by electron microscopy, and the change of acid-consuming capacity with passing of time was determined by the method of pharmacopoeia of Korea. The results of these studies are summerized as follows: 1. The grain size was linearly enlarged as the time goes by. The aluminium hydroxide gel gradually crystallized in a certain period of time. 2. The acid-consuming capacity was in exponential function, decreased as the grain size of them enlarged. 3. One particle consists of tens of grains.4. Grinding the Sample obtained in any period of testing time in mortar did not change both their grain size and their acid-consuming capacity. 5. The grain size of dried aluminium hydroxide gel ought to be micronized less than $100{AA}$ for maintaining the ability such as consumes 250m1 of 0. 1N-HC1 solution per Is of $Al(OH)_3$ described in pharmacopoeia of Korea.