The effects of the stretching speed and the swelling degree of cocoon filaments on load-elongation curve were tested by tensilon with special attachments. The values of breaking strength, elongation at break and initial tensile strength obtained from load elongation curves are summarized as follows; 1. The breaking strength of the swollen cocoon filament appeared to increase at the high stretching speed, while elongation at break decreased. 2. Load-elongation curve became crinkled at the low speed of stretching. It suggests that both slip and break of the macrofibrils may occur in swelling of cocoon bave. 3. Breaking strength appeared to considerably decrease and elongation at break not to increase in swelling test at 9$0^{circ}C$ for 60 min. 4. The initial tensile strength was influenced by the stretching speed and swelling degree of cocoon filaments.