Proposals were mode on how to differentiate radiation effects in morphological phases of polyethylene and discussions were developed with the results obtained on a low density polyethylene, SOCAREX, specified by number average molecular weight; overbar Mn=5,400, density; 0.92, and degree of branch; 3.4/100 carbon atom, which was irradiated to Co$^{60}$ .gamma. ray at the dose rate of 0.5 Mrad/hr in ambient temperature under the pressure of 10$^{-5}$ Torr. or 1 atm. respectively. The effect to crystalline phase in possibly deduced from dose dependent variation of relative area between (110) and (200) peaks on X ray diffraction spectrum and that, the effects to amorphous phase can be understood through dose dependent relaxation behaviours of .betha. peak on internal friction characteristics of the specimen. The results obtained thus far indicate that, in crystalline phase, relative crystallinity shows a rather rapid decrease up to 20 Mrad with increasing dose, however, little change of crystallinity can be observed in the region between 20-200 Mrad, and degradation appears to be more predominant than crosslinking up to 60 Mrad. While in amorphous phase the indication also shows that degradation is only predominant up to 20 Mrad. Furthermore several correlations can be seen with amenable explanation between dose dependent behaviours observed in both phases.