This study was attempted in order to search for physical properties of sail cement. In this study, soil samples were specified according to soil particle analysis and used for compaction, strength, abrasion, absorption tests respectively according to different cement contents. Cement content sused in each treatment were 6%, 8%, 10% and 12% of total weight of soil-consent mixture. In the test, compressise strengths of the specimens were measured at the following ages; 3 days, 7-days, 14-days, 21-days and 28-days. Abrasion and absorption tests of the specimens were carried out at the 7-days age only. The results obtained from the tests are summarized as follows; 1. As the cement contents were in creased, the compressive strengths of soil-cement were almost proportionally increased. 2. The Compressive strength of soil-cement was not always proporportional to ages. The gradient of compressive strength of the soil-cement was steeper as the cement content was rucreased. 3. As the cement content was increased, the amount of the weight loss of the samples due to the abrasion was decreased remarkably, giving no abrasion for about 8% of the cement content. 4. As the cement content was increased, the absorption ratio of the specimens was not changed remarkably.