For the manufacture of the silver-yellow glass, silver nitrate was used as a colorant in the base glass of $K_2O$-CaO-$SiO_2$ system. The latter in which the optimum condition was revealed showing beautiful yellow color had been selected among others after the preparatory studies to choose base glass. Other base glass systems considered were $Na_2O$-CaO-$SiO_2$, $R_2O$-PbO-$SiO_2$ and $R_2O$-PbO-BaO-$SiO_2$. The color developed on the specimen in various conditions was examined, using spectorphotometer, in term of the changes in absorbance with wavelength in the visible range. Experimental variables were the amount of the colorant and the additives, reheating temperature and time. The additives such as ZnO, BaO, $B_2O_3$ and $As_2O_3$ were added to increase the coloring action. It was observed that as the amount of silver increased in the base glass the absorbance around $410{mu}m$ showed the increasing tendency, but the width of absorption curve was wider. Hence, the optimum amount of silver appeared to be 0.11~0.12%. It was found that ZnO was effective additive when present about 0.1%, while $As_2O_3$ ineffective rather retarding the coloration. Borax and $BaCO_3$ were proved effective when contained separately, but appeared ineffective when coexisted. Proper reheating temperature and time was ranged 550~$580^{circ}C$ and 50~60 minutes. The higher the reheating temperature and the longer the reheating time, the absorbance was increased, while the width of absorption curve was wider. The colored glass prepared in the present experimental condition was found to have good water-resistance for the decorative purpose.