In this work the effect of pre-rolling on the homogenization and on the mechanical properties of 4.6% Mg-0.5% Mn-0.18% Cr-Al alloy has been studied. At room temperature tensile strength and elongation have been found to increase in the pre- rolled homogenized sample compared to those of the as cast sample. At $400^{circ}C$ this pre-rolled homogenized sample has shown a little lower tensile strength and a remarkably higher elongation than the samples as casted or homogenized without pre-rolling. Metallurgical microstructure of the pre-rolled homogenized sample has shown conspicuously less secondary phase such as ${eta}$-phase at the grain boundaries than the other samples. The difference of magnesium content between grain boundaries and within the grains has been also checked by EPMA. The test results show enhanced homogenizing effect by the pre-rolling before homogenizing heat treatment.