The study was carried out to investigate the variations in the fibroin hydrolysis of different cocoon shell layers, and the relationship between the hydrolysis and silk physical property. The obtained results are as follows: 1. The fibroin hydrolyzing ratio was highest at the inner layer of cocoon shell and. next in order. at the middle layer and at the outer layer. 2. The fibroin hydrolyzing ratio of abnormal cocoons was higher than normal cocoon and it was different among them, tile highest was double coroon, thin shell cocoon and perforated cocoon in order. 3. The sericin content and fibroin hydrolyzing ratio of Jam 111 and Jam 112 was higher than that of Jam 111 $ imes$ Jam 112. 4. The fibroin hydroiyzing ratio of the cocoons fed with the artificial diets was increased at the inner layer. The sericin content of those lessened at the inner layer, however, it slightly increased at the most inner layer more than at the inner layer. 5. The breaking strength of the degummed silk fiber of different cocoon layers was reduced at the inner layer. The breaking Strength of abnormal silk fiber was less than that of normal silk fiber. 6. A negative correlation (r= －0.8) )was approved between fibroin hydrolyzing ratio and breaking strength of silk fiber, and the regression line was Y=－0.29x＋5.07.