In this study, we are observe to the sagger which is composed of cordierite-mullite system. And especialy, we investigated the characteristics of the body which composed of Chamotte-Kaolin-Plastic clay-Talc (or Clinochlore) system and Chamotte-Kaolin-Plastic clay-Agalmatolite-Talc (or Clinochlore) system. The obtained results are as follows. 1. Modulus of rupture and apparent porosity were improved by particle size of talc and clinochlore in order that -16 mesh, -6 mesh, 6-16 mesh. 2. When the body composed of talc, the modulus of rupture was increased as firing temperature was rising up but composed of clnochlore, it was reversed. 3. When added to the agalmatolite, firing shrinkage, modulus of rupture and apparent porosity were improved. 4. Mineral phases of samples fired at 125$0^{circ}C$ above consist of cordierite, mullite and $alpha$-cristobalite.