Hadong Kaolin (Halloysite) was granulated cylindrically and treated with 1N aqueous sodium hydroxide solution for 6-48 hrs at 60-10$0^{circ}C$. The crystalling structure of surface of the products was studied by X-ray powder diffraction method. The reaction rate of halloysite to sodium A zeolite showed a gradual decrease from surface to inner layer. At the surface layer, the reaction mechanism was observed as first order consecutive reaction as follows: halloysitelongrightarrowamorphous aluminosilicatelongrightarrowsodium A zeolitelongrightarrowhydroxysodalite By applying the above reaction mechanism, the rate constants and activation energies was measured.