The effect of $Ti^{+4}$ addition on the sinterability, microstructure, and temperature dependence of electromechanical coupling factor of magnetostrictive Ni-Cu-Co ferrite was investigated. The density of Ni-Cu-Co ferrite slightly increased by 2.0 mole % addition of either $TiO_2$ or $Fe_2TiO_4$, but tended to decrease by more than 2.0 mole % addition of $TiO_2$ or $Fe_2TiO_4$. As the content of either $TiO_2$ or $Fe_2TiO_4$ increased, the magnetocrystalline anisotropy compensation temperature also increased. Microstructure studies showed the stable grains when Ni-Cu-Co ferrite was sintered above 1, 20$0^{circ}C$.