In order to investigate the utilization of industrial waste and briquette ash for concrete production, briquette ash was used as fine aggregate for mortar production and three different kinds mortars were produced by mixing carbide and bottom aches with cement. These products were compared with mortar, produced by standard sand, in the respects of compressive, tensil and bending strengths. Further study on the economic aspect of utilization of briquette ash is needed but the results obtained from our preliminary study are summarized as follows : 1. The compressive strengths at the age of seven days of mortars, made of one to two ratios of cement to briquette ash, (cement+carbide ash) to briquette ash and(cement+bottom ash) to briquette ash were 70%, 61% and 58%, respectively, of the mortar made of standard sand. The compressive strengths of those mortars at the age of 28 days were 56%, 49% and 48% of the mortar made standard sand. 2. The compressive strengths at the age of seven days of the mortar made of one to two ratios of cement to briquette ash, (cement+carbide ash) to briquette ash and (cement+bottom ash) to briquette ash were 84%, 73%, and 70% of the mortar which was produced according to Korean Standard Value. The compressive strengths of those mortars at the age of 28 days were 85%, 73% and 73% of the mortar of the Korean Standard value. 3. The tensil strengths at the age of seven days of the mortars made of one to two ratios of cement to briquette ash, (cement+carbide ash) to briquette ash, and (cement+bottom ash) to briquette ash were 64%, 36%, and 36%, respectively, of the mortar of standard sand. The tensil strengths of those mortars at the age of 28 days were 70%, 47%, and 39%, respectively, of the standard mortar. The mortars made of one to two ratios of cement to briquette ash at the age of seven and 28 days were higher than the mortars of Korean Standard. The other mortars were 61 to 62% at the age of seven days and 75 to 90% at the age of 28 days of the Korean Standard mortar, respectively. 4. The bending strengths at the age of seven days of mortar made of one to two ratios of cement to briquette ash, (cement+carbide ash) to briquette ash, and (cement+bottom ash) to briquette ash were 46%, 53% and 50% of the mortar of standard sand. The bending strengths of those mortars at the age of 28 days were 90%, 77% and 69%, respectively of the mortar of standard sand. 5. The mortar of briquette ash which was lower in strengths compared with the mortar of cement have shown possibility of its secondary products of cement and concrete. The uses of briquette ash and industrial waste as construction materials would contribute toward solving various pollution problems caused by industrial wastes and saving labor costs needed to cleaning up. Furthermore, the effective use of briquette ash would greatly save the aggregate resources.