The sintering phenomena and piezoelectric properties of PZT ceramics of composition $Pb(Zr_{0.54} Ti_{0.46})O_3$ were investigated when a small quantity of $La_2O_3$ , $LaMnO_3$, $LaCrO_3$ were added. The unwanted chemical composition change in PZT during sinterin porces du to PbO evaporation poses a severe problem in PZt manufacturinig. It is observed tat an addition of small amount of $LaMnO_3$ to PZT markedly decreases the evaporation of PbO during sintering . The green compact of (1-x) PZT.xLaMnO3(x=0.02~0.10) could be sintered of under O2 atmosphere alone with no significant loss of PbO. The planar coupling factor kp of the sintered $0.98Pb(Zr_{0.54} Ti_{0.46})O_{3.0.02}LaMnO}3$ is similar to that of commercial PZT 6A. Microstructure investigation shows that part of sintering process of $Pb(Zr, Ti)O_3$.$LaMnO_3$ system progresses via liquid phase sintering. It is believed that the evaporation of PbO in PZT sintering is restricted by the addition of $LaMnO_3$ due to the above phenomena. Furthermore the solid solution of $LaMnO_3$ in PZT causes diffuses phase transition.