The castable refractory, CaO.$2Al_2O_3$ is a useful alumina cement for iron, steel and cement for iron, steel and cement industries, however it is difficult to produce CaO.$2Al_2O_3$because of its high melting point(180$0^{circ}C$) and narrow firing range. In this study, the coprecipitation method was used to produce CaO.$2Al_2O_3$ for lower temperature firing . This method involved the titration of mixed solution of calicum and aluminate which extracted from domestic kaolin with $NH4_OH$ solution under blowing $CO_2$ gas into the solution. The coprecipitate and its clacined products were analyzed by X-ray diffraction and DTA. The calcined products fired between 400 and 90$0^{circ}C$ were amorphous, but at 100$0^{circ}C$ the coprecipitate was converted into one compound, CaO$2Al_2O_3$. From those experimental results, it was found that we could synthesizze CaO.$2Al_2O_3$ at about 100$0^{circ}C$ which is lower than conventional firing temperature by around 80$0^{circ}C$. The refractoriness of this alumina cement was SK 34 and the compressive strength ( 1 day) was about 250kg/$ extrm{cm}^2$.