The purpose of this dissertation is to study the physical properties of cellular rubber products for industrial use. Vulcanization characteristics were investigated by usingcure curve that had obtained by means of Rheometer. The results of physical properties, vulcanization characteristics and foaming states are as follows. 1. The test results for vulcanization characteristics of NR compounds indicated that in the recipe R-1. When accelerator D is used, the optimum conditions of vulcanizate are obtained, while formula R-2 and R-3 have shown higher torgue at curing time, $1{sim}2$ minutes. Cellular rubber product test in terms of compression set and compression deflection has also met the requirements of SAE. 2. For SBR compounds, S-1 formula was the best in terns of vulcanization characteristics, and for the blowing structure of cellular rubber products, formula S-3 in which accelerator M is added was fair. All other test results, such as compression set and compression deflection properties met SAE requirements. 3. NBR compound (N-1) including accelerator TT was the best in terms of vulcanization characteristic and also blowing structure. All other properties listed above met requirements, particulary for oil resistance test. 4. In the test of EPDM compounds, when mixed accelerator, M and TT, is used(formula E-1) the best results were obtained. Since EPDM is hydrocarbon elastomer, oil resistance test failed. All other properties met the requirement specified in SAE.