The fishing hooks were tested for breaking and unbending due to plastic deformation of the material. Study of tensile test is not complicated, but has not even worked out fully enough, especially when the test specimen is subjected to plastic deformation. The fishing hook is subjected to unbending stress and the critical section is a Point which is furthest from the line of action of the forces. The dynamic force of fish during jerks depends on their speed of movement and body weight, the kinetic energy corresponding to it and also on the rlastic displacement of the rigging which absorb the energy. Six kinds of hook were tested by the dynamometer under tensile speed 290mm/min (subscript s) and 780mm/min (subscript f). According to their results, the breaking load(B: kg) can be induced with the formula $B={alpha}wd^2+eta$ where w(mm) is the distance between the barb base and the lower shank and d(mm) is diameter. The coefficients of the formula for the round hooks(R) and the angular hooks(A) are approximately as follows: $$R:;alpha_{s}=0.5,;eta_{s}=1.6,;alpha_{f}=0.4,;eta_{f}=1.4$$ $$A:;alpha_{s}=1.1,;eta_{s}=2.0,;alpha_{f}=1.0,;eta_{f}=0.9$$ The ratio of $B_{f};to;B_{s}$ is corresponding to 0.8. The ratio of deformation(X) that is moved distance of barb base at break to the distance(H) between head base and barb base is about $50\%$. Further study should be carried out on the subject of impact and fatigue test under the same condition which is exerted force by the hooked fish.