This experiment was made on the basis of the general observation that silk fabrics is flaccid in sun light. The purpose of this test is to examine efficiency between the processed thread and the unprocessed one after putting the later under the xenon-lit system, which produces continuous spectrum of bright white beam similar to sun light. (i) Color division of silk thread : white, yellow blue (ii) light division and irradiation time : sun lightlongrightarrow210 hrs, Xenonlongrightarrow50,100, 150 hrs. Under the above conditions each object was be tested with and extensometer, TENSILON Type III for the results of (a) the weight-expansibility curve of the silk thread (b) the relationship between cutting in tensity and maximum, weight (c) maximum expansion rate (d) the expansion energy of the tested silk thread (e) the beginning pull-stretch resistance rate of the tested silk thread (f) color difference after processing The results are illustrated in the appropriate tables and figures. Consequently the generalobservation that silk fabrics is flaccid is relevant only in terms of color. So for as Cutting-intensaty is concerned, it turned out to be less flaccid than in color. On the contrary when the untested silk thread was conpared with the xenon-irradiated ones, the latter proved itself to be more flaccid in cutting expansibility than the former. We have learned through this experiment that, after the all rounds of this test, the color tone and chroma of the colored materials remained without significant change, where as their color value changed to a large extent.