The fatigue crack propagation behavior or non-heat-treatment and thermally aged type 304 stainless steel was investigated on the basis of linear elastic fracture mechanics. This Study was concentrated on the relations between the crack propagation rate and the stress intensity factor range. The following results are obtained : The precision measurement and observation of fatigue crack propagation behavior is studied with moire grating. The effect of thermally aged type 304 stainless steel is investigated under small load. In the equation da/dN=c(.DELTA. k)/SUP m/, factor m of thermally aged steel is a little higher than non-heat-treatmented steel and its limit is m=1.35-4.2.