The purpose of this study is to investigate the free edge delamination of the laminated composites under uniaxial strain. The laminate is modeled as a set of anisotropic layers with isotropic adhesive layers. Interlaminar stresses are calculated for laminate with various laminate parameters by using two dimensional finite difference method. The redistribution of interlaminar stresses after delamination and the relation between delamination any ply failure are obtained for [.+-.45.deg.]$_{s}$, [0.deg./.+-./.+-.45.deg./90.deg.]$_{s}$ and [0.deg./45.deg./90.deg/45.deg.]$_{s}$ laminates. It was found that delamination can not propagate the entire width of the laminate under the static loading condition.ition.