For the preparation of ferroxidure BaO.5.5 $Fe_2O_3$ with high coercive force, the green and calcined coprecipitates, which were obtained by neutralizing the mixed salt solution $FeCl_2-BaCl_2$ and $FeCl_3-BaCl_2$ with alkali solution $NaOH-Na_2CO_3$, were investigated about the thermal reaction, crystal growth, and the magnetic properties of the sintered specimens. The very single-domain crystallites of Ba-ferrite with high coercive force are formed from the coprecipitate of amorphous $Fe(OH)_3$ and amorphous $BaCO_3$ at lower temperature than that of subnucleus crystalline $delta$-FeOOH and amorphous $BaCO_3$