The effects of $MnO_2$ and $Cr_2O_3$ on the Piezoelectrictric properties of Pb(Mg1/2W1/2)0.3 Ti0.4 Zr0.3O3 Ceramics. Electromechanical properties in the system in connection with the sintering temperature and the effects of $MnO_2$ and $Cr_2O_3$ addition. The dielectric constant of the ceramics decreased with the additions of $MnO_2$ while the additions of $Cr_2O_3$ increased the value. The Planar coupling factor (Kp) of the ceramics with 0.2wt% $MnO_2$ and with 0.2wt% $Cr_2O_3$ gave the highest value of 0.52 and 0.513 as sintered at 106$0^{circ}C$, 108$0^{circ}C$, respectively. The value of mechanical Q-factor were in parallel with the fired density of the ceramics. The optical micrography of the sintered bodies showed that the additions of $MnO_2$ promoted the grain growth, while the additions of $Cr_2O_3$ retarded the grain growth.