An in vitro study was conducted to compare the bond strength of cements between Verabond coping and various cores. Fifty-four idential cores simulating maxillary central incisor prepared for PFM crowns were made. Eighteen samples were made with 20K cast gold, eighteen with Verabond, and eighteen with Adaptic. Samples were randomly divided into three groups, each consisting of six 20K cast gold, six verabond, and six Adaptic samples. The first group was cemented with zinc phosphate cement, the second group with poly-carboxylate cement, and the third group with glass ionomer cement. Constant finger pressure was applied for cementation. The sample were then stored at $37^{circ}C$ in distilled water bath for 24 hours. The tensile strength test was performed on an Instron Universal test machine with crosshead speed of 0.05cm/min and the results compared statistically. Results of the study showed that: 1. A significant difference of bond strength was observed with different types of dental cements and core materials. 2. With gold core, zinc phosphate cement was stronger than both the polycarboxylate cement and glass ionomer cement, which did not differ in bond strength. 3. With base-metal core, zinc phosphate cement showed the highest bond strength and was followed by polycarboxylate cement and glass ionomer cement. 4. With composite resin core, zinc phosphate cement showed the highest bond strength and was followed by glass ionomer cement and polycarboxylate cement. 5. The base-metal core (Verabond core) privided the highest retention of all core materials.